Chemically activated shaped carbon, process for producing same and use thereof

ABSTRACT

A chemically activated shaped carbon suitable for adsorbing and desorbing hydrophobic organic compounds and having the specific properties in bulk density, pore volume, bulk density x pore volume, surface area, bulk density x surface area, mean pore size and the effective amount of adsorption of butane, a process for producing thereof and use thereof.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a chemically activated shaped carbon, a process for producing the activated carbon and use thereof.

2. Description of the Prior Art

It has been conventional practice to recover organic solvents from gases containing the organic solvent as vaporized, by passing the gas through a layer of shaped activated carbon to cause the carbon adsorb the organic solvent, and thereafter heating the active carbon layer to desorb the adsorbed solvent.

When gasoline engines for motor vehicles are stopped during driving, the heat of the engine operating at a high temperature is released to the environment to bring about a so-called hot-soaked state, permitting evaporation of gasoline. An active carbon layer is used for adsorbing the gasoline vapor and releasing the adsorbed gasoline for reuse for the operation of the engine.

It is desired that the activated carbon for use in these activated carbon layers be shaped carbon having high working capacity (the amount of effective adsorption) and high durability.

However, the conventional activated carbon for such uses is still unsatisfactory in the amount of effective adsorption, physical strength, etc.

Examined Japanese Patent Publication SHO 50-39635 discloses shaped activated carbon for adsorbing heavy metal ions, such as chromium ion, contained in waste liquids. The disclosed carbon is one obtained by chemically activating an organic material such as lauan flour with phosphric acid U.S. Pat. No. 2,508,474 discloses chemically activated granular carbon, which is suitable for use as gas mask adsorbent. However, both references do not disclose specifically the physical properties of the product obtained. Further, the both references do not disclose that the activated carbon obtained can be used for the adsorption and desorption cycle of gases.

SUMMARY OF THE INVENTION

The main object of the present invention is to provide shaped activated carbon suitable for adsorbing and desorbing hydrophobic organic compounds and having high owrking capacity and high durability, a process for industrially advantageously producing such shaped activated carbon by the chemical activation method, and uses thereof.

Accordingly, the present invention provides a chemically activated shaped carbon suitable for adsorbing and desorbing hydrophobic organic compounds and having the properties of 0.25 to 0.6 g/cm³ in bulk density, 0.5 to 1.2 cm³ /g in pore volume, 0.25 to 0.4 cm³ /cm³ in bulk density x pore volume, at least 1000 m² /g in surface area, at least 400 m² /cm³ in bulk density x surface area, 18 to 35 angstroms in means pore size and 5.0 to 15 g/100 ml in the effective amount of adsorption of butane. The present invention further provides a process for producing a chemically activated shaped carbon which comprises heating and reacting at 100° to 160° C. a mixture of a chemically activatable starting material and 40 to 70 % aqueous solution of a chemical in a ratio of 1/0.6 to 1/3.0 by dry weight of their respective solid, shaping the reaction mixture at a temperature of 90° to 160° C. when a total weight of the reaction mixture has become 90 to 115% of a dry weight of solids in the mixture before heating, and thereafter calcining, washing and drying the shaped product by conventional methods to obtain a shaped activated carbon.

According to the present invention, various materials can be made into shaped activated carbons which are great in the amount of effective adsorption per unit volume, outstanding in durability and suitable for adsorbing and desorbing hydrophobic organic compounds.

The shaped activated carbon of the present invention is suited to the recovery of hydrophobic organic compounds and is desirable, for example, for use in gasoline evaporation preventing devices (Evaporated Loss Control Device; ELCD) and the like.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows the principle of operation of a gasoline evaporation preventing device as an example in which the shaped activated carbon of the invention is used, diagram (a) showing the device during adsorption and diagram (b) showing the same during desorption; and

FIG. 2 is a flow chart illustrating the basic feature of a solvent recovery process as another example in which the present shaped activated carbon is used.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

The starting carbon material to be used in the present invention is a chemically activatable material. Examples of such materials are cellulosic materials (e.g., wood chips and coconut shells) and starch materials (e.g., cereals including corn, millet, foxtail millet and barnyard millet). Of these, cellulosic materials are desirable. Examples of chemicals useful for the chemical activation method are those generally used for activation, such as phosphoric acid, zinc chloride, calcium chloride and the like, among which zinc chloride and phosphoric acid are desirable. Zinc chloride is more desirable.

The term "bulk density" as used herein for the shaped activated carbon of the invention refers to the bulk density of 10- to 28-mesh (according to old JIS abolished in March 1987) shaped activated carbon as determined according to the method of JIS K 1474.The shaped activated carbon of the invention is generally 0.25 to 0.6 g/cm³, preferably at least 0.3 g/cm³, more preferably at least 0.35 g/cm³, in bulk density.

The term "pore volume" refers to the amount of N₂ adsorbed as determined by the N₂ adsorption method at a relative pressure of 0.931 and is used for pore volumes of up to 300 angstroms as determined by the Cranston-Inkley method. The shaped activated carbon of the present invention is generally 0.5 to 1.2 cm³ /g, Preferably at least 0.6 cm³ /g, more preferably at least 0.65 cm³ /g, in pore volume. The pore volume can be determined using, for example, a device of CARLO ERBA SORPTO MATIC SERIES 1800.

The shaped activated carbon of the invention must further fulfill the requirement that the product of the bulk density multiplied by the pore volume should be in the range of 0.25 to 0.4 cm³ /cm³. When the product is in this range, the activated carbon has high adsorptive capacity per unit volume and excellent strength. The product is preferably at least 0.27 cm³ /cm³, more preferably at least 0.29 cm³ /cm³.

With the shaped activated carbon of the invention, the surface area thereof is determined by the BET method. The carbon is generally at least 1000 m² /g, preferably at least 1100 m² /g, more preferably at least 1300 m² /g, in surface area. With the activated carbon of the invention, the surface area is further limited in its relationship with the bulk density. More specifically, the product of the bulk density multiplied by the surface area is generally at least 400 m² /cm³, preferably at least 500 m² /cm³, more preferably at least 550 m² /cm³. The surface area can be measured with use of the same device as mentioned above for the determination of the pore volume.

The mean pore size of the shaped activated carbon of the invention is a value calculated from the pore volume and the surface area The present carbon is generally 18 to 35 angstroms, preferably 19 to 30 angstroms, more preferably 20 to 28 angstroms, in mean pore size.

Butane working capacity of the carbon of the present invention is a value determined for 100 ml of a sample of the carbon with use of n-butane having a purity of at least 99.9%. The method of determination will be described in detail in Example 1 to be given later. The present activated carbon is generally 5.0 to 15 g/100 ml, preferably 8.0 to 15 g/100 ml, more preferably 9.0 to 15 g/100 ml, in the effective amount of butane adsorbed as determined by this method.

In particle size, the shaped activated carbon of the invention is suitably plus 50 mesh (as determined according to JIS using a screen with an opening size of at least 0.3 mm), preferably plus 36 mesh (using a screen with an opening size of at least 0.425 mm), more preferably plus 30 mesh (using a screen with an opening size of at least 0.5 mm).

The chemically activated shaped carbon of the present invention is suitable for adsorbing and desorbing hydrophobic organic compounds. The hydrophobic organic compounds to be adsorbed and desorbed are preferably those having solubility in water of up to 10 wt. % at 20° C. and a boiling point of -5° C. to 170° C. Examples of such hydrophobic organic compounds are chain aliphatic saturated o unsaturated hydrocarbons having 4 to 8 carbon atoms (hereinafter expressed as "C₄ -C₈ "), C₅ -C₉ alicyclic hydrocarbons, C₆ -C₉ aromatic hydrocarbons, C₁ -C₆ hydrocarbon halides, C₄ -C₈ ethers, C₅ -C₇ ketones, C₃ -C₈ esters, etc.

More specific examples of such C₄ -C₈ chain aliphatic saturated or unsaturated hydrocarbons are n-butane, n-pentane, n-hexane, isohexane, n-heptane, n-octane, isooctane(2,2,4-trimethylpentane), 2,2-dimethylbutane, 2-pentene and the like.

Examples of such C₅ -C₉ alicyclic hydrocarbons are cyclohexane, methylcyclohexane and the like.

Examples of such C₆ -C₉ aromatic hydrocarbons are benzene, toluene, o-xylene, m-xylene, p-xylene ethylbenzene, isopropylbenzene and the like.

Examples of such C₁ -C₆ hydrocarbon halides are methylene chloride, chloroform, carbon tetrachloride, ethyl chloride, ethylene chloride, ethylidene chloride, 1,1,1-Lrichloroethane, 1,1,2-trichloroethane, 1,1,1,2-tetrachloroethane, 1,1,2,2-tetrachloroethane, pentachloroethane, vinylidene chloride, 1,2-dichloroisopropyl chloride, allyl chloride, 1,2-dichloropropane, butyl chloride, amyl chloride, o-chlorotoluene, p-chlorotoluene and the like.

Examples of such C₄ -C₈ ethers are ethyl ether, n-butyl ether, epichlorohydrin, diglycidyl ether, furan and the like.

Examples of such C₅ -C₇ ketones are methyl n-propyl ketone, methyl n-butyl ketone, methyl isobutyl ketone, methyl n-amyl ketone, diethyl ketone, ethyl n-butyl ketone, cyclohexanone, o-methylcyclohexanone and the like.

Examples of such C₃ -C₈ esters are ethyl formate, propyl formate, n-butyl formate, isobutyl formate, amyl formate, ethyl acetate, n-propyl acetate, isopropyl acetate, n-butyl acetate, isobutyl acetate, sec-butyl acetate, n-amyl acetate, isoamyl acetate, ethyl butyrate and the like.

The starting material for preparing activated carbon by the process of the invention is a chemically activatable material, which is preferably a celluosic material such as coconut shells, wood chips, saw dust or the like. Chemicals useful for activation are those generally used as such and already mentioned, among which zinc chloride and phosphoric acid are preferable, and more preferable is zinc chloride.

With the process of the present invention, the activating chemical is used in the form of a 40 to 70 wt. % aqueous solution Concentrations less than 40 wt. % are not desirable since the reaction then requires a longer period of time. Concentrations over 70 wt. % present difficulty in uniformly mixing the starting carbon material and the activating chemical together, permit the reaction to proceed at a very high velocity and make it difficult to control the reaction. The carbon material and the aqueous chemical solution are mixed together in the ratio generally of 1/0.6 to 1/3.0, preferably 1/0.8 to 1/2.0, by dry solids weight.

The mixture of starting carbon material aqueous solution of activating chemical is heated at 100° to 160° C. for reaction The term "reaction" as used herein refers to the preparation of a black substance from the starting carbon material by decomposing and dehydrating the material under the action of the activating chemical.

The reaction must be conducted at a temperature of at least 100° C. to effect the removal of water. At a higher temperature, the reaction proceeds at a higher velocity, whereas at temperatures exceeding 160° C., the reaction proceeds excessively, making it impossible to shape the resulting reaction mixture.

With the process of the invention, the end point of the reaction is critical. One of the features of the present invention is to terminate the reaction at such a stage that the reaction mixture is most suited to shape. We have found it desirable to discontinue the reaction when the weight of the reaction mixture has become 90 to 115% of the dry weight of the starting mixture (dry weight of the starting carbon material +dry weight of the activating chemical). The term the "reaction mixture" refers to all the substances or materials present in the reaction system inclusive of water Simultaneously when the starting carbon material becomes black, tar is formed which is thought to act as a binder during shaping and during activation through calcining, so that the reaction, if allowed to proceed excessively, eliminates the tar, makes the reaction mixture difficult to shape and fails to give shaped activated carbon retaining hardness and having a compact structure on calcining and activation. On the other hand, if the reaction is terminated too early, the reaction mixture contains a lesser quantity of tar and still retains a large amount of water, permitting the water to remain between the particles during shaping, with the result that the activated carbon obtained on calcining and activation is low in bulk density and in compactness.

Next, the reaction mixture is compactly shaped while being deaerated. The mixture is shaped while being heated at 90° to 160° C., whereby the tar resulting from the reaction is melted and allowed to remain between the particles as a binder, consequently giving a compacted shaped product

If the mixture is shaped at a temperature below 90° C., the tar will not melt, failing to diffuse through the clearances between the particles and rendering the mixture difficult to shape. Furthermore, the product obtained upon calcining and activation is liable to disintegrate into particles When the temperature is above 160° C., the liquid portion (tar and water) of the reaction mixture becomes separated from the solid portion thereof during the shaping step This renders the mixture difficult to shape.

In the shaping step, the reaction mixture is deaerated by applying a pressure thereto with or without evacuation. A tableting machine, press, extruder or the like is used as the shaping device. While the foregoing conditions are employed for the mixture to be press-shaped with respect to the shaping temperature and the reaction end point, it is suitable in the case of extrusion that the shaping temperature be 90° to 130° C. and that the weight of the reaction mixture at the end point of the reaction be 100 to 115% of the dry weight of the starting mixture (dry weight of the starting carbon material +dry weight of the activating chemical). The shaped product can be in the form of tablets, plates, pellets, briquettes or the like, as optionally determined. Crushed type activated carbon can be obtained by crushing shaped activated carbon.

The shaped product is calcined for activation and then washed with an acid by methods which are generally employed for producing chemically activated carbon. For example, the product is calcined for carbonization in a rotary kiln at 500° to 700° C. for 10 minutes to 1 hour and is thereby activated, followed by washing and drying, whereby shaped activated carbon can be prepared.

The chemically activated shaped carbon obtained by the above process fulfills the foregoing requirements as to the properties such as bulk density, pore volume, surface area, mean pore size and effective amount of adsorption of butane.

The active carbon of the present invention can be further activated with a gas and thereby increased in the effective amount of adsorption of butane. The gas activation can be effected in the same manner as in the usual process for producing gas-activated shaped carbon. For example, water vapor or carbon dioxide is used as the activating gas at a gas partial pressure of 30 to 60% for calcining the carbon at 850° to 1000° C. for 10 minutes to 4 hours.

The chemically activated shaped carbon of the present invention is suitable for recovering hydrophobic organic compounds, such as those mentioned above, by repeated adsorption and desorption The activated carbon is therefore usable, for example, for gasoline evaporation preventing devices (FIG. 1) for gasoline engines, solvent recovery processes (FIG. 2), etc.

In the FIG. 1, 1 is activated carbon layer, 2 and 3 each are pressure regulating valves, 4 is intake manifold, 5 is gas tank, 6 is exhaust manifold, 7 is air cleaner, 8 is gas flow In the FIG. 2, 11 is activated carbon layer, 12 is condenser, 13 is separator, 14 is steem, 15 is gas containing solvent, 16 is solvent, 17 is water, 18 is exhaust.

EXAMPLES

The present invention will be described in greater detail with reference to the following examples, which nevertheless in no way limit the invention

EXAMPLE 1

Dry saw dust (1.3 kg) and 2.6 kg of an aqueous zinc chloride solution having a concentration of 50% were heated with stirring The temperature of the mixture gradually rose to exceed 100° C., whereupon the mixture started to undergo a reaction with the evaporation of water. The reaction was allowed to proceed to prepare a black reaction mixture. Portions of reaction mixture with varying weights were obtained by changing the end point of the reaction. More specifically, reaction mixture portions were obtained which were altered from 82 to 136% stepwise in weight relative to the dry weight (taken as 100%) of the starting mixture of saw dust and zinc chloride solution.

With heating at 130° C., the reaction mixture was shaped into disks (30 cm in diameter and about 4 mm in thickness) by a press or shaped into tablets (5 mm in diameter and about 3 mm in thickness). The shaped pieces were placed into a crucible and calcined at 600° C. for 3 hours for activation.

The calcined product was washed with hydrochloric acid and then with water for the removal of zinc chloride, and was thereafter dried in the conventional manner. The dried product was crushed to 10 mesh to 28 mesh and checked for properties. Table 1 shows the results.

The experimental results (bulk density, crushing yield, shape) indicate that good results can be achieved when the weight at the reaction end point and the reaction temperature are 90 to 115% and up to 160° C., respectively.

                                      TABLE 1                                      __________________________________________________________________________     Exper-   End- Max. temp.                                                                            Bulk                                                                               Crushing                                              iment                                                                              Shaping                                                                             point                                                                               during density                                                                            yield                                                 No. method                                                                              wt. (%)                                                                             reaction (°C.)                                                                 (g/l)                                                                              (%)  Shape                                            __________________________________________________________________________     1-1 Press                                                                                82  170    334 58   No shape retentivity,                                                          readily became powder                            1-2 "     85  165    374 64   Partly became powdery                            1-3 "     94  150    401 72   Hard, slightly became                                                          powdery                                          1-4 "    102  130    443 73   Very hard, remained in                                                         shape                                            1-5 "    111  125    441 73   Very hard, remained in                                                         shape                                            1-6 "    118  120    407 71   Slightly brittle, remained                                                     in shape                                         1-7 "    130  115    373 72   Brittle, not became powdery                      1-8 "    136  115    320 66   No shape retentivity, not                                                      became powdery                                   1-9 Tableting                                                                            82  170    336 62   Readily became powdery                            1-10                                                                              "     89  160    404 73   Hard, slightly became                                                          powder                                           __________________________________________________________________________

The activated carbons of Exp. Nos. 1-4 and 1-5 were checked for the effective amount of adsorption of n-butane by the method stated below The results are given below

    ______________________________________                                         (Results)                                                                                             Experiment No.                                                                 1-4   1-5                                               ______________________________________                                         Amount of n-butane adsorbed (g/100 ml)                                                                  16.1    16.0                                          Amount of remaining n-butane (g/100 ml)                                                                 7.2     7.2                                           Effective amount of adsorption of                                                                       8.9     8.8                                           n-butane (g/100 ml)                                                            ______________________________________                                    

The effective amount of adsorption of n-butane was determined by the following method. 1. The sample is dried at 150° .C for 3 hours and then cooled to room temperature in a desiccator. 2. The sample is packed in a glass column, 15.4 mm in inside diameter, to a height of 10 cm. 3. The column is sealed off, and the weight is measured (A g). 4. With the column set in a constant-temperature water bath at 25° C., n-butane (at least 99.9% in purity) is passed through the sample at a flow rate of 250 mg/min for 15 minutes (up flow). 5. The column is removed and checked for the weight (B g). 6. The column is then set in the device again, and dry air is passed through the sample (down flow) at 190 ml/min at 25° C. (10 BED vol/min) for 20 minutes. 7. The column is removed and checked for the weight (C g). 8. The above steps 4 to 7 are repeated four times, and the averages for 2 to 4 cycles are calculated. ##EQU1## B=average of B values for 2 to 4 cycles e,ovs/C/ (g)=average of C values for 2 to 4 cycles

V (ml)=volume of the sample

EXAMPLE 2

The same reaction mixture as prepared in Example 1, 102% in weight at the end point of reaction, was shaped into disks by a press at varying temperatures 50° to 200° .C The same procedure as in Example 1 was thereafter repeated to obtain shaped activated carbon, which was then checked for properties Table 2 shows the results.

                  TABLE 2                                                          ______________________________________                                               Shaping  Bulk    Crushing                                                Exp.  temp.    density yield                                                   No.   (°C.)                                                                            (g/l)   (%)    Shape                                            ______________________________________                                         2-1    50      *       44     Readily became powdery                           2-2    70      341     57     Brittle, partly became                                                         powdery                                          2-3    90      420     71     Hard, remained in shape                          2-4   110      431     72     Very hard, remained in                                                         shape                                            2-5   130      443     73     Very hard, remained in                                                         shape                                            2-6   160      440     71     Very hard, remained in                                                         shape                                            2-7   170      393     63     Became partly powdery                            2-8   200      373     60     Readily became powdery                           ______________________________________                                          Note                                                                           *Not measureable because the carbon collapsed into powder.               

At 170° C. and 200° C., the liquid portion separated off. The reaction mixture was hardened at the portions thereof close to the press plates but became brittle at its central portion between the press plates.

The shaped activated carbons of Exp. Nos. 2-3, 2-4, 2-5 and 2-6 were checked for the effective amount of adsorption of n-butane in the same manner as above. The results are as follows.

    ______________________________________                                         (Results)                                                                                      Experiment No.                                                                 2-3  2-4      2-5    2-6                                       ______________________________________                                         Amount of n-butane adsorbed                                                                      15.2   15.6     16.1 16.0                                    (g/100 ml)                                                                     Amount of remaining n-butane                                                                     6.9    7.0      7.2  7.2                                     (g/100 ml)                                                                     Effective amount of adsorption of                                                                8.3    8.6      8.9  8.8                                     n-butane (g/100 ml)                                                            ______________________________________                                    

EXAMPLE 3

Dry coconut shell flour and an aqueous solution of zinc chloride were heated at 120° to 130° C. with stirring for reaction (The proportion of zinc chloride was varied as shown in the table below, Nos. 1 to 8.) The reaction was terminated when the weight of each reaction mixture became 90 to 115% of the dry weight of the starting mixture, and the resulting reaction mixture was shaped into disks (30 cm in diameter and about 4 mm in thickness) at 130° C. by a press, then placed into a crucible and calcined at 600° C. for 3 hours for activation.

In the usual manner, each calcined product obtained was washed with hydrochloric acid and then with water for the removal of unreacted zinc chloride, and was thereafter dried.

The dried products (shaped activated carbons Nos. 1-8) where crushed to 10 mesh to 28 mesh and checked for properties Table 3 shows the results.

                                      TABLE 3                                      __________________________________________________________________________     Effects of zinc chloride                                                                                              Press-shaping                           Shaped activated carbon No.                                                                       1  2  3  4   5  6   7   8                                   __________________________________________________________________________     Coconut shell flour                                                                          [g]  1300                                                                              1300                                                                              1300                                                                              1300                                                                               1300                                                                              1300                                                                               800 800                                 Zinc chloride ["]  780                                                                               1040                                                                              1170                                                                              1300                                                                               1430                                                                              1625                                                                               1200                                                                               1600                                Water         ["]  780                                                                               780                                                                               1040                                                                              1300                                                                               1040                                                                              1300                                                                               1200                                                                               1200                                Coconut shell flour                                                                          [part]                                                                              100                                                                               100                                                                               100                                                                               100 100                                                                               100 100 100                                 Zinc chloride ["]  60 80 90 100 110                                                                               125 150 200                                 Water         ["]  60 60 80 100 80 100 150 150                                 Endpoint weight                                                                              [g]  2030                                                                              2150                                                                              2415                                                                              2887.3                                                                             2709                                                                              3286.1                                                                             1987.1                                                                             2390                                  "           [%]  97.6                                                                              91.9                                                                              97.8                                                                              111.1                                                                              99.2                                                                              112.3                                                                              99.4                                                                               99.6                                Bulk density  [g/l]                                                                               540                                                                               479                                                                               452                                                                               441 440                                                                               377 369 325                                 Surface area  [m.sup.2 /g]                                                                        1102                                                                              1315                                                                              1354                                                                              1458                                                                               1399                                                                              1473                                                                               1310                                                                               1466                                Pore volume   [ml/g]                                                                              0.513                                                                             0.618                                                                             0.653                                                                             0.717                                                                              0.726                                                                             0.804                                                                              0.879                                                                              1.066                               Mean pore size                                                                               [Å]                                                                             18.6                                                                              18.8                                                                              19.3                                                                              19.7                                                                               20.8                                                                              21.8                                                                               26.8                                                                               29.1                                Surface area  [m.sup.2 ml]                                                                        595                                                                               630                                                                               612                                                                               643 616                                                                               555 483 476                                 Pore volume   [ml/ml]                                                                             0.277                                                                             0.296                                                                             0.295                                                                             0.316                                                                              0.319                                                                             0.303                                                                              0.324                                                                              0.346                               Amount of n-butane                                                                           [g/100 ml]                                                                          14.0                                                                              15.2                                                                              15.2                                                                              16.0                                                                               16.6                                                                              15.3                                                                               15.5                                                                               16.5                                adsorbed                                                                       Amount of remaining                                                                          ["]  7.9                                                                               7.4                                                                               7.1                                                                               7.2 6.9                                                                               5.6 4.6 4.2                                 n-butane                                                                       Effective amount of                                                                          ["]  6.1                                                                               7.8                                                                               8.1                                                                               8.8 9.7                                                                               9.7 10.9                                                                               12.3                                adsorption of n-butane                                                         __________________________________________________________________________

Consequently, as the proportion of zinc chloride increased, the mean pore size increased, the pore volume increased and the bulk density decreased because of the increase in the pore volume.

(For reference, common carbon prepared from coconut shells and activated with water vapor is up to 6.0 g/100 ml in the effective amount of adsorption of n-butane, and other activated carbons commercially available and great in the effective amount of adsorption of n-butane are about 8 g/100 ml in this value.)

The mean pore size (angstroms) was calculated from [4×pore volume (ml/ml)/surface area (m² /ml)]×10⁴.

EXAMPLE 4

Dry saw dust (10 g) and 20 g of 50% aqueous solution of zinc chloride were thoroughly mixed together with a spurtle in a 500-c.c. beaker, held in a constant-temperature dryer for 24 hours and then checked for the resulting change in weight (i.e. the weight of the resulting mixture based on the dry weight of the starting mixture of saw dust and zinc chloride, as expressed in percentage) and also for the degree of reaction. This procedure was repeated at varying dryer temperatures of 70° to 200° C. as listed in Table 4, which also shows the results.

                  TABLE 4                                                          ______________________________________                                              Dryer                                                                     Sam- temp.      Weight  Degree of reaction                                     ple  (°C.)                                                                              (%)     (state of mixture)                                     ______________________________________                                         A     70        134     No reaction                                            B     80        129     No reaction                                            C     90        128     Slightly became black but no                                                   progress in reaction                                   D    100        111     Became black                                           E    110         91     "                                                      F    130         83     "                                                      G    150         82     "                                                      H    200         82     "                                                      ______________________________________                                    

Each mixture was then shaped into tablets (6 mm in diameter and about 3 mm in thickness) with heating at 130° C. as in Example 1. Although samples C, D and E were shapable samples A, B, F, G and H were not shapable. Samples C, D and E were calcined at 600° C. for 1 hour for activation, whereby samples D and E were each made into shaped activated carbon of high strength, whereas sample C gave a product which was low in strength and brittle.

EXAMPLE 5

Dry saw dust (1.3 kg) and 2.6 kg of an aqueous zinc chloride solution having a concentration of 50% were heated with stirring. The temperature of the mixture, rising gradually, was controlled by varying the degree of vacuum. The reaction mixture was then shaped with a press in the same manner as in Example 1, calcined in a crucible at 600° C., washed with acid and water, crushed and checked for properties. Table 5 below shows the results, which indicate that reaction temperatures of above 100° C. afford good results.

                                      TABLE 5                                      __________________________________________________________________________     Exper-                                                                             End- Max. temp.                                                                            Bulk                                                                               Crushing                                                   iment                                                                              point                                                                               during density                                                                            yield                                                      No. wt. (%)                                                                             reaction (°C.)                                                                 (g/l)                                                                              (%)  Shape                                                 __________________________________________________________________________     4-1 123   87    --  --   Not shapable                                          4-2 106   89    --  --     "                                                   4-3 102   90    --  --     "                                                   4-4 104   94    303 45   No shape retentivity,                                                          readily became powdery                                4-5 107  102    432 71   Very hard, remained in                                                         shape                                                 4-6 105  106    441 74   Very hard, remained in                                                         shape                                                 4-7 119  113    386 69   Slightly brittle, but not                                                      became powdery                                        4-8 103  122    441 72   Very hard, remained in                                                         shape                                                 __________________________________________________________________________

The activated carbons with Exp Nos. 4-5, 4-6 and 4-8 given above were checked for the effective amount of adsorption of n-butane by the method a)ready described. The results are as follows.

    ______________________________________                                         (Results)                                                                                          Experiment No.                                                                 4-5   4-6    4-8                                           ______________________________________                                         Amount of n-butane adsorbed (g/100 ml)                                                               15.7    16.1   16.0                                      Amount of remaining n-butane (g/100 ml)                                                              7.0     7.1    7.2                                       Effective amount of adsorption of                                                                    8.7     9.0    8.8                                       n-butane (g/100 ml)                                                            ______________________________________                                    

EXAMPLE 6

The active carbon prepared in Example 3 using 110 parts of zinc chloride was further activated with water vapor under the conditions of Table 6 below. Table 6 also shows the properties of the product. The activation with water vapor for 1.5 hours increased the amount of n-butane adsorbed and the effective amount of adsorption of n-butane by about 12%.

                                      TABLE 6                                      __________________________________________________________________________     Influence of activation (ZnCl.sub.2 110 parts)                                 __________________________________________________________________________     Activation temperature (°C.)                                                            950  950  950   950                                            Activation time (hr)                                                                           0.0  0.5  1.0   1.5                                            Charge (g)      150.0                                                                               150.0                                                                               150.0 150.0                                          Output (g)      123.8                                                                               121.0                                                                               95.3  84.2                                           Yield (%)       82.5 80.7 63.5  56.1                                           Yield (heat treatment base, %)                                                                 100.0                                                                               97.7 77.0  68.0                                           Bulk density (g/l)                                                                             463  450  387   363                                            Surface area (m.sup.2 /g)                                                                      1273 1363 1620  1758                                           Pore volume (ml/g)                                                                             0.653                                                                               0.723                                                                               0.889 0.987                                          Mean pore size (angstroms)                                                                     20.5 21.2 22.0  22.5                                           Surface area (m.sup.2 /ml)                                                                     589  613  627   638                                            Pore volume (ml/ml)                                                                            0.302                                                                               0.325                                                                               0.344 0.358                                          Amount of n-butane adsorbed                                                                    17.4 15.7 17.9  18.6                                           (g/100 ml)                                                                     Amount of remaining n-butane                                                                   7.8  7.3  7.7   7.7                                            (g/100 ml)                                                                     Effective amount of adsorp-                                                                    9.6  8.4  10.2  10.9                                           tion of n-butane (g/100 ml)                                                    __________________________________________________________________________

EXAMPLE 7

Shaped activated carbon No. 8 prepared in Example 3 was tested for equilibrium adsorption of the five kinds of organic solvents listed below. The amount of equilibrium adsorption (wet %) was determined at 25° C. and 100° C. using nitrogen containing 0.1 vol. % of each organic solvent. The condition of 25° C., 0.1 vol. % is typical of usual conditions under which common organic solvents are adsorbed The condition of 100° C., 0.1 vol. % is typical of usual conditions under which common organic solvents are desorbed Accordingly, the greater the difference (effective amount of adsorption) in the amount of adsorption between 25° C. and 100° C., the more suitable is the activated carbon for the recovery of organic solvents.

For comparison, activated carbon (particulate SHIRASAGI (S₂ ×4/6)) for recovering usual solvents was also similarly tested. Table 7 below shows the results.

                  TABLE 7                                                          ______________________________________                                         Active carbon                                                                              No. 8          Comparative                                         N.sub.2 containing 0.1                                                                     25° C.                                                                           100° C.                                                                           25° C.                                                                         100° C.                           vol. % of solvent                                                                          (wet %)  (wet %)   (wet %)                                                                               (wet %)                                  ______________________________________                                         Cyclohexane 40.5     6.0       25.7   11.7                                     MIBK*       58.8     7.4       37.3   16.4                                     n-Heptane   45.9     8.5       29.1   17.7                                     p-Xylene    59.6     13.4      37.8   28.3                                     Benzene     45.4     6.1       28.8   11.6                                     ______________________________________                                          *MIBK: methyl isobutyl ketone                                            

The above results reveal that shaped activated carbon No. 8 is greater than the comparative activated carbon in the effective amount of adsorption of any of the organic solvents. 

What is claimed is:
 1. A process for producing a chemically activated shaped carbon suitable for adsorbing and desorbing hydrophobic organic compounds which comprises heating and reacting at 100° to 160° C. a mixture of a chemically activatable starting material selected from the group consisting of coconut shells, wood chips and saw dust, and 40 to 70% aqueous solution of an activating chemical comprising zinc chloride in a ratio of 1/0.6 to 1/3.0 by dry weight of their respective solid content, shaping the reaction mixture at a temperature of 90° to 160° C. when the total weight of the reaction mixture has become 90 to 115% of the dry weight of the solids in the mixture before heating, thereafter calcining, washing and drying the shaped product by a conventional method followed by further activating the shaped product with a gas to thereby obtain a shaped activated carbon, said shaped activated carbon having such properties that it has a bulk density of 0.25 to 0.6 g/cm³, a pore volume of 0.5 to 1.2 cm³ /g, a bulk density x, pore volume of 0.25 to 0.4 cm³ /cm³, a surface are of at least 1000 m² /g, a mean pore size of 18 to 35 angstrones, a bulk density x surface area of at least 400 m² /cm³, and which adsorbs butane in an amount of 5.0 to 15 g/100 ml.
 2. A process according to claim 1 wherein the product is shaped by pressing.
 3. A process according to claim 1 wherein the product is shaped by extrusion.
 4. A process according to claim 1 wherein the gas is water vapor or carbon dioxide.
 5. A process according to claim 4 in which the gas is used at a partial pressure of 30 to 60% for calcining the shaped carbon at a temperature of 850° C. to 1000° C. for a period of from 10 minutes to 4 hours. 